Submerged Welding flux SJ-101

The Submerged Welding flux SJ-101 produced by GUJIN® is the perfect choice for all your industrial needs. We are a reliable and trustworthy manufacturer that offers high quality products at favorable prices. As a wholesale supplier of SJ-101 fluxes, we are committed to providing you with the best products and best customer service.

Model:SJ-101

Send Inquiry

Product Description

GUJIN® is Submerged Welding flux SJ-101 manufacturers and suppliers in China who can wholesale Welding flux SJ101. GJ.SJ 101 is a kind of fluoride-al kaline-type sla g-serial sintered flux, mesh 10-60(2-0.3mm).it has great capacity of sulphur removal,phosphor removal and anti-rust. The technology has good d performance, easy to desla g and with fine appearance of weld,even in the narrow gap of deep slope entrance. The metal weldin g seam has good plasto-toughness, with low diffusion of hydro gen and fine cold and heat crack resistance.

Usage:

It can be applied to different we'lding wires and is fit for welding of low-carbon steel and low alloy steel. Moreover, it can b e used for fast welding of pipeline steel and for welding of thick waffstructures of different high-tensile steel.

Cautions:

1.The oil soil,moisture,iron rust and other foreign substances must be removed from the welding joint.

2.It is better to use direct arrrent.

3. The welding flux must be baked under 300-350℃ for 2 hours.

Chemical Composition (%)

SiO₂+TiO₂	Al₂O₃+MnO	CaO+MgO	CaF₂	S	P
15-20	25-30	25-30	15-20	≤0.05	≤0.05

Basicity of the Flux：B//W=1.6-1.8

Mechanical Performance of the Deposited Metal

Wire	Standard Modeis	Yield Strength （MPa）	Tensile strength(MPa)	Impact energy AKV(J)	Elongation
H08A	F4A2-H08A	≥340	≥420	≥27（-20℃）	≥22%
H08MnA	F5A4-H08MnA	≥410	≥490	≥27（-40℃）	≥22%
H08Mn2MoA	F7021-H08Mn2MoA	≥500	≥600	≥27（-20℃）	≥17%